Low specific wear rate under high load and low speed versus steel, ie. bearings/bushings

Properties

PropertyNominal Value1UnitTest Method
PhysicalDensity1.38g/cm3ISO 1183
Water Absorption0.2%ISO 62
Mold Shrinkage (t3mm, Φ100mm)2%KEP (Flow Direction)
MechanicalTensile Strength58MPaISO 527
Elongation at Yield10%ISO 527
Nominal Strain at Break33%ISO 527
Flexural Strength80MPaISO 178
Flexural Modulus2400MPaISO 178
Notched Charpy Impact Strength5.5kJ/m2ISO 179
ThermalMelt Flow Rate11g/10minISO 1133
Melting Point165ºCISO 3146
HDT(1.8MPa)89ºCISO 75
Coefficient of Linear Thermal Expansion13x10-5/ºCISO 11359
ElectricalSurface Resistivity1 × 1016ΩIEC 60093
Volume Resistivity1 × 1014Ω . mIEC 60093
FlammabilityFlame RatingHBUL 94

1Typical properties: these are not to be construed as specifications.

Automotive OEM Approvals

ManufacturerSpecificationNotes
GM-KoreaEDS-M-5203

Disclaimer: The information contained herein is based on our current knowledge and experience for above product, made by Korea Engineering Plastics Co., Ltd. (“KEP”) as delivered in the original package. This information should not be construed as a promise or guarantee of specific properties of this product described or its suitability to their purpose prior to use this product. It is sole responsibility of the users to investigate whether any existing patents are infringed by the use of this product. This product is not intended for use either in medical or a dental implant. Users should meet all safety and health standards. Any intellectual property rights are observed.